液相沉淀-煅烧法制备大粒径球形四氧化三钴

以硫酸钴为原料,碳酸氢铵为沉淀剂,采用液相沉淀法合成了大粒径球形碳酸钴,考察了不同晶种量、pH和硫酸钴溶液流量对碳酸钴形貌、粒度分布、振实密度和硫元素质量分数的影响,并探究了碳酸钴的生长机理。通过分步煅烧,并设置不同升温时间使碳酸钴热分解,得出优化四氧化三钴理化指标的煅烧条件。结果表明,当晶种量为2 kg,pH在7.2～7.5,硫酸钴溶液流量为500 mL/h时,采用分段式热分解碳酸钴,各温区按统一时间(60 min)升温,所得四氧化三钴形貌为球形,中值粒径为16.52μm,振实密度达2.26 g/cm3。     

Cross-linked anion exchange membranes with flexible,long-chain,bis-imidazolium cation cross-linker

Herein, poly (phenylene) oxide (PPO)-based cross-linked anion exchange membranes (AEMs) with flexible, long-chain, bis-imidazolium cation cross-linkers are designed and synthesized. Although the cross-linked membranes possess high ion exchange capacity (IEC) values of up to 3.51–3.94 meq g⁻¹, they have a low swelling degree and good mechanical strength because of their cross-linked structure. Though the membranes with the longest flexible bis-imidazolium cation cross-linker (BMImH-PPO) possess the lowest IEC among these PPO-based AEMs, they show the highest conductivity (24.10 mS cm⁻¹ at 20 °C) and highest power density (325.7 mW cm⁻² at 60 °C) because of the wide hydrophilic/hydrophobic microphase separation in the membranes that promote the construction of ion transport channels, as confirmed by atom force microscope (AFM) images and the small angle X-ray scattering (SAXS) analyses. Furthermore, the BMImH-PPO samples exhibit good chemical stability (10% and 6% decrease in IEC and conductivity, respectively, in 2 M KOH at 80 °C for 480 h, and a 22% decrease in weight in Fenton's reagent at 60 °C for 120 h), making such cross-linked AEMs potentially applicable in alkaline anion exchange membrane fuel cells.     

A numerical model to predict the powder–binder separation during micro-powder injection molding

The micro-powder injection molding (micro-PIM) process has the potential to bridge the gap between the design and manufacturing of micro-components that are often used in small and handy devices. Numerical modeling helps to analyze and overcome various difficulties of micro-PIM. In the present work, a numerical model is developed to predict the powder–binder separation (a common defect in PIM and especially severe in micro-PIM) during the injection of an alumina feedstock. A powder–binder separation criterion is proposed dealing with applied injection pressure and friction force between the powder and binder. An indirect comparison of feedstock travel time between two locations is used to validate the model. The predicted segregation from the simulated result is supported by a qualitative experimental measurement. The developed model can be used to optimize injection parameters to get a defect-free product.     

Approaching Ultrastable High‐Rate Li–S Batteries through Hierarchically Porous Titanium Nitride Synthesized by Multiscale Phase Separation

Porous architectures are important in determining the performance of lithium–sulfur batteries (LSBs). Among them, multiscale porous architecutures are highly desired to tackle the limitations of single‐sized porous architectures, and to combine the advantages of different pore scales. Although a few carbonaceous materials with multiscale porosity are employed in LSBs, their nonpolar surface properties cause the severe dissolution of lithium polysulfides (LiPSs). In this context, multiscale porous structure design of noncarbonaceous materials is highly required, but has not been exploited in LSBs yet because of the absence of a facile method to control the multiscale porous inorganic materials. Here, a hierarchically porous titanium nitride (h‐TiN) is reported as a multifunctional sulfur host, integrating the advantages of multiscale porous architectures with intrinsic surface properties of TiN to achieve high‐rate and long‐life LSBs. The macropores accommodate the high amount of sulfur, facilitate the electrolyte penetration and transportation of Li⁺ ions, while the mesopores effectively prevent the LiPS dissolution. TiN strongly adsorbs LiPS, mitigates the shuttle effect, and promotes the redox kinetics. Therefore, h‐TiN/S shows a reversible capacity of 557 mA h g^?1 even after 1000 cycles at 5 C rate with only 0.016% of capacity decay per cycle.     

A Review on the Separation of Niobium and Tantalum by Solvent Extraction

Niobium and tantalum are found together in natural minerals. Leaching with concentrated acid solution or alkaline roasting followed by water/dilute acid leaching results in a solution containing these two metals. In this work, we reviewed the extraction and separation of Nb(V) and Ta(V) from leach liquors in the absence and presence of hydrofluoric acid by acidic, neutral extractants and amines. Several solvent extraction systems were compared in the light of the requirement of hazardous chemicals, extraction/separation efficiency, and stability/solubility of extractants. Since the cationic species of Nb(V) and Ta(V) are unstable in the aqueous solution, the application of acidic extractants for extraction and separation of these metals is limited. Amines can extract Nb(V) as well as Ta(V) irrespective of the presence of fluoride ion but the separation of these metals from the loaded amines should be carried out in stripping process, resulting in process complexity. Another disadvantage encountered for amine is related to high viscosity in extraction process. Neutral extractants are considered as promising extractants which are effective to separate Ta(V) and Nb(V) from either non-fluoride or to moderate fluoride ion concentration in terms of extraction, separation and stripping efficiency. Compared to the traditional methyl iso-butyl ketone (MIBK) based system, methyl isoamyl ketone (MIAK) is found to be a promising extractant to separate Nb(V) and Ta(V).     

共价有机框架材料及其在关键核素分离中的应用进展

共价有机框架材料（COFs）是一类由共价键连接的多孔晶态材料。因具有单体链接方式灵活、结构可调、活性位点丰富、比表面积大、理化性质相对稳定等特点，它们在气体储存与分离、能量储存、催化和光电学领域受到了广泛的关注。本文主要从结构设计、合成方法及功能化、材料的分析表征和晶形控制等方面概括地介绍了COFs材料。在此基础上，综述了COFs材料在关键核素分离方面的研究进展，并展望了其在核素分离领域的应用前景和今后的研究方向。     

钚及其裂变产物钯 、银 、镉 、锡 、锑 、锆的系统分离方法

描述了钚及其6种裂变产物钯、银、镉、锡、锑、锆的系统分离方法：在强碱性阴离子交换树脂柱上将盐酸介质的辐照靶溶解液中的这些元素分为5组，然后再针对各组目标元素进行分离和纯化，可简便快速地从同一份靶溶解液中分离以上7种元素。采用辐照铀靶对分离方法进行了验证，结果表明，分离流程对6种裂变产物的化学回收率均大于70%，对γ谱仪测量干扰的主要核素去污因子均大于1.0×10³，可满足²³⁹Pu裂变谷区核素裂变产额测量对化学分离的要求。     

转底炉处理赤泥工艺技术

为了综合利用氧化铝冶炼产生的赤泥，探索在转底炉中直接还原赤泥、磨矿磁选获得高品位直接还原铁。通过实验室试验摸索了转底炉还原工艺参数，并在转底炉工业试验线进行了工业试验。实验室结果表明，赤泥还原后的直接还原铁(DRI)金属化率可达88.6%，磁选后的铁品位可达82.1%，磁选后的铁回收率可达88.9%。工业试验中，转底炉还原后，产品金属化率平均为69.2%，将还原后的DRI磁选获得高品位的DRI产品，磁选后DRI的铁品位为72.8%，磁选后铁回收率达到了85.2%,初步打通了在转底炉中还原赤泥、磁选的工艺路径。